集料性状对高强混凝土断裂和声发射特性的影响
张立新1，吕伟民1，陈兵2，吴科如2
(1.同济大学道路与交通工程系，上海200092；2.同济大学混凝土材料研究国家重点实验室,上海200092）
摘要:计算不同粗集料粒径、不同集料体积率和不同种类粗集料混凝土断裂能和断裂韧性；测试混凝土断裂时的声发射事件数；分析了集料性状对混凝土断裂性能的影响以及声发射事件数和断裂性能的关系。
关键词:混凝土；高强混凝土；集料；裂纹；声发射
中图分类号: TU528.31 文献标识码: A 文章编号: 0253-374X(2001)05-0546-05
Effects of Aggregates ' Character on Concrete Fracture
Performance and Acoustic Emission
ZHANG Li-xing1, LU Wei-min1, CHEN Bing2, WU Ke-ru2
(1. Department of Road and Traffi Engineering, Tongji University ,Shanghai 200092 ,China;
2. The State Key Laboratory of Concrete Research, Tongji University .Shanghai 200092 .China)
Abstract: The tests were carried out to study the effect of the size and type of and the volume rate of aggregates on fracture energy and toughness of high-strength concrete (HSC) and the hits of acoustic emission inthree-point bending (AE) fracture toughness testing. The relationship between fracture properties of concreteand AE hits was analyzed.
Key words: concrete; high-strength concrete(HSC) ; aggregate; crack; acoustic emission(AE)
集料是混凝土的重要组成部分，通常占混凝土总体积的75%以上，构成了混凝土骨架，因此其在一定程度上决定了新拌混凝土流变性、硬化混凝土强度以及混凝土耐久性[1]。
以前研究集料对混凝土力学性能影响时，研究对象为普通混凝土。普通混凝土由于界面强度低,混凝土破坏都是发生在界面,集料的特性影响不大。高强混凝土则由于界面得以加强,混凝土破坏可能切断集料，因而集料的特性对其影响较大；而且以前的研究手段较为单一，主要针对混凝土强度，本文利用混凝土的荷载—挠度曲线和混凝土声发射事件图研究混凝土断裂性能。近年来，工程使用的混凝土的强度越来越高，所以研究集料对高强混凝土断裂性能的影响对于提高混凝土的性能具有重要意义。
1试验设计