尿素合成塔检测技术
黄源 李光海
(中国石油化工股份有限公司广州分公司，广州510726) (中国特种设备检测研究中心，北京100013)
摘 要：综述了尿素合成塔在使用过程中可能出现的腐蚀和缺陷形态，并根据失效的可能性给出了有效的检测方法，包括宏观检查、厚度检测、磁粉检测、渗透检测、硬度检测、声发射检测、金相检查和金属磁记忆检测等技术。分别介绍了这些无损检测方法的特点，以及如何在尿素合成塔检验中进行实施。
关键词：尿素合成塔；腐蚀；无损检测；综述
中图分类号：TG115.28 文献标识码：A 文章编号：1000-6656(2007)11-0674-05
Inspection and Nondestructive Testing Technique on Urea Synthesizer
HUANG Yuan LI Guang-hai
(SINOPEC Guangzhou Petrochemical Complex．Guangzhou 510726，China)
(china Special Equipment Inspection＆Research Center．Beijing 100013，China)
Abstract：Various corrosions and defects possibly emerged in urea synthesizer were presented.The effective nondestructive testing(NDT)method according to damage mechanisms and mode of failure were also put forward．The applied NDT methods included visual testing，thickness measuring，magnetic particle testing，penetration testing hardness testing．acoustic emission testing。metallographic analysis and metal magnetic memory testing．The application situation and characteristic of each NDT method applied in urea synthesize tower were introduced．
Keywords：Urea synthesizeri;Corrosion；Nondestructive testing；Survey
1 问题的提出
尿素合成塔(以下简称合成塔)除早期少数采用单层卷焊结构外，其余绝大部分为多层包扎结构。就制造和使用而言，合成塔有如下特点：①制造过程中采用层板包扎工艺，筒节对接以及与封头的组对采用深环焊缝结构，焊后一般不进行热处理，有较大的残余应力。②操作工况苛刻：高温高压且反应中间产物有很强的腐蚀性，反应气体中，还含有H2等，有潜在的爆炸危险。③长期处于有应力和腐蚀倾向的介质环境中。所以合成塔在制造和使用过程中，常常会产生各种缺陷，并在使用过程中不断扩展。因此，采用合理的检测技术对在役的合成塔进行全面检验，有着十分重要的意义[1-3]。
2 尿素合成塔腐蚀和缺陷
合成塔内壁衬里主要出现的是各种腐蚀缺陷和衬里焊缝的焊接缺陷。由于衬里的主要作用是隔离介质与碳钢强度层的接触，所以对内衬的检验主要以发现局部异常腐蚀为主，对于碳钢层板的强度层，是用来承受内压等载荷的，检验的重点是为了发现制造或使用过程中产生的，可能引起筒体整体强度削弱的危险性缺陷，如裂纹等。